FabCO® 95K2
Excellent for high tensile strength and low temperature impact properties that are needed. The basic slag formulation also ensure that the weld deposit will be low in diffusible hydrogen. Provides great fracture toughness, increased toughness at low temperature and increased resistance to cracking.
AWS: A5.29: E90T5-K2C H4/-K2M H4
SDS: English (NA), Spanish (NA), French (NA), English (EU), Spanish (EU), French (EU)
Certification: Download PDF
Approvals: CE
Product Sizes & Specifications
| Part Number | Diameter (IN) | Diameter (MM) | Package | Base Metal | Welding Process | Welding Position |
|---|---|---|---|---|---|---|
| S659519-029 | 1/16 | 1.6 | 33 Lb (15 Kg) Spool | low alloy | FCAW (flux cored) | flat/horizontal |
Industries
Can be used for welding several HSLA and quench and tempered steels like ASTM A710, A709 Gd HPS70W, A514, and HY 80. Shipbuilding, Offshore, Heavy Equipment
Applications
Single or multiple pass applications with 100% CO2 or 75Ar/25CO2 shielding gas
Similar Products
-
FabCO® 81N1
1% nickel deposit. Used in applications where low temperature notch toughness is required. Can be used on weathering types of steel where color match is not required.
-
FabCO® 101K3
Offers excellent properties on many higher strength steels.
-
FabCO® 105D2
This product can be used for the repair of manganese-moly castings, or components that must undergo post weld heat treatment and maintain a tensile strength in the neighborhood of 100,000 psi. The basic slag system ensures a low hydrogen weld deposit.
-
FabCO® 115
Primarily used in the welding of T-1, A514, A517, HY-100, and similar quenched and tempered high strength and low alloy steels. The basic slag system produces a low hydrogen weld deposit reducing the chance of cracking.
-
FabCO® 115K3
This wire is used for welding high strength quench and tempered and low alloy steels like T-1, A514, A517, and Hy-100. The T-5 flux core uses a basic slag which keeps hydrogen content very low reducing the chance for cracking.
-
FabCO® 125K4
For the welding of quenched and tempered low alloy grades of steels. Excellent impact values at low temperatures along with a low diffusible hydrogen content due to the basic slag system.